100% virgin monofilament polypropylene fiber for concrete
Elite’s Polypropylene fiber mono. is a high performance
monofilament Polypropylene fiber specifically develop as a crack
control additive for concrete. It reduces the occurrence of plastic
shrinkage and settlement cracks, while enhancing the surface
properties and durability of hardened concrete.
The fiber are extremely fine, single filament and coated with
special compound to aid dispersion that enable excellent dispersion
of individual filament, allowing the formation of a homogeneous
three-dimensional matrix with the concrete mix.
It is suited to reinforce and crack-resist to every kinds of cement
concrete and mortar, specially used in engineering of building
surface, floor, wall etc…..
|Raw Material||Polypropylene||Crack Elongation||20+/-5%|
|Fiber Type||monofilament||Fiber Diameter||20um-30um|
|Melting Point(C Deg.)||160 - 170||Density(g/cm3)|
|Acid &Alkali Resistance||Strong||Tensile Strength(MPa)||450 min.|
Times of 4mm
|Normal length||4mm, 6mm, 8mm, 12mm,18mm, 24mm, 30mm etc...|
◆ Resist to shrink & crack ◆ Increase seepage resistance
◆ Increase friction resistance ◆ Increase freezing & thawing
◆ Improve tendons protection ◆ Replace steel net (using in
◆ Prevent mortar split and crackle expansion
◆ Increase impact resistance and peeling resistance
A). No agglomeration and easily spread around in mortar or
concrete. Guarantee the property of crack resistance effectively
B). Apply conveniently. No need to change the proportion of mortar,
and just put the fibers into the mortar mixture and stir for a
moment after adding water.
C). Has fine economic property. The equivalent dia. of
polypropylene monofilament is only φ 25um, so the ratio of dia. and
surface is high and on the basis of crack resistance, it can reduce
the amount (0.6kg/m 3 ) and cut down the cost effectively.
D). Be better to plaster. Because a great number of thin fibers
spread into mortar evenly, so the plastering is much easier and
this can improve the binding strength between surface and base.
E). The fiber has stable chemical property, strong acid &alkali
resistance, and can be used in any engineering projects.
A). suit for the waterproof layer, floor, inner & outer wall of
industrial and civil construction.
B). Increase cracking resistance on the surface of industrial
workshop, warehouse and parking lot.
C). Increase cracking & seepage resistance of the ground in
swimming pool, pond and ditch.
D). Suit for any mortar projects and common concrete projects.
E). Highway, bridge and other roads.
4. Applying Instruction:
A). Dosage: for resist the common cracks on surfaces, 0.9kg/m3
fibers to cement mortar is enough, and for increasing reinforce and
seepage resist application 1.8kg/m3 is enough.
B). Stirring requirement: The proportion of cement, sand and
aggregate is no need to be changed. Put cement, aggregate, additive
and fiber together, then stir after adding enough water and time
for stirring can be prolonged for 2~3 minutes in order to make the
compound mix completely. Also it can be mixed with cement and other
aggregates in advance, stirring by adding water at work site before
0.6kg, 0.9kg or 1.0kg a PE film bag or water soluble paper bag;
18kgs/carton or 20kgs/plastic woven bag.